| 項 目 Property | * 位 Unit | 試驗方法 Test Method | 試驗*件 Test Condition | AX4000 |
| 抗張強(qiáng)度 Tensile Strength | kg/cm2 ( MPa) | ASTM D-638 ( ISO527) | 23℃ | 400 ( 39) |
| 彎曲強(qiáng)度 Flexural Strength | kg/cm2 ( MPa) | ASTM D-790 ( ISO178) | 23℃ | 700 ( 69) |
| 彎曲模數(shù) Flexural Modulus | kg/cm2 ( MPa) | ASTM D-790 ( ISO178) | 23℃ | 26000 ( 2450) |
| 洛式硬度 Rockwell Hardness | R-Scale | ASTM D-785 ( ISO2039/2 ) | 23℃ | R-106 |
| Izod衝*強(qiáng)度 Izod Impact Strength | kg-cm/cm ( J/m ) | ASTM D-256 ( ISO R180 ) | 23℃ 1/4’’ 厚 | 17 ( 167) |
| *變形溫度 Heat Deflection Temperature | ℃ | ASTM D-648 (ISO 75/A) | Unannealed 18.6kg/cm2 ( 1/2’’ 厚 ) | 99 |
| Annealed 18.6kg/cm2 ( 90 ℃×8Hr) | 110 | |||
| *氏軟化* Vicat Softening Point | ℃ | ASTM D-1525 (ISO 306) | 1 Kg Load | 116 |
| 熔融指數(shù) Melt Flow Index | g/10 min | ASTM D-1238 ( ISO1133 ) | 220℃×10Kg ( 98N ) | 10 |
| 收縮率 Molding Shrinkage | % | FCFC Method | 23℃ | 0.4~0.7 |
| 比 重 Specific Grity | ASTM D-792 ( ISO1183 ) | 23℃/23℃ | 1.05 | |
| 燃燒性 Flammability | UL-94 | FILE NO. E162823 | 1/16" HB All Color |