新光TPEE DH6000

SHINITE? S201NA DH6000 TPEE Base polymer Grade / Nature TPEE 一般級(jí) / 本色 Unit Test Method Values Mechanical properties 機(jī)械性* Izod Impact(Notched) 衝*強(qiáng)度 Kg-cm/cm ASTM D256 NOT BREAK Tensile Strength at Yield 降伏強(qiáng)度 Kg/cm2 ASTM D638 219 Tensile Strength at Peak 拉伸強(qiáng)度 Kg/cm2 ASTM D638 > 360 Nominal Tensile Strain at Break 拉伸率 % ASTM D638 > 480 Flexural Strength 彎曲強(qiáng)度 Kg/cm2 ASTM D790 180 Flexural Modulus 彎曲模數(shù) Kg/cm2 ASTM D790 3400 Hardness (Shore D) 蕭氏硬度 - ASTM D2240 63 Thermal properties * 性 * Heat Deflection Temperature *變形溫度 ASTM D648 66psi °C - 264psi °C - Flammability 防火性 - UL94 HB Melting Point 熔* °C DSC 212 Melt Index 230°C/2.16Kg 熔融指數(shù) g/10min ASTM D1238 20 Electrical properties **性* Dielectric Strength 介*強(qiáng)度 KV/MM ASTM D149 26 Dielectric Constant 介*常數(shù) … ASTM D150 - Volume Resistivity ***阻 Ω-CM ASTM D257 1.00E+16 Other properties 其它性* Specific Grity 比重 - ASTM D792 1.23 Water Absorption 吸水率 % ASTM D570 0.5 Mold Shrinkage 成形收縮率 ASTM D955 Flow 流*方向 % 1.5 Cross Flow 垂直方向 % 1.5 Injection Molding 成型*件 INJECTION MACHINE 成型機(jī)臺(tái) OZ 3 DRYING 乾燥 4-5 HR × 80 (℃) BARREL TEMPERATURE 成型溫度 °C REAR 205-215 MIDDLE 215-225 FRONT 225-235 NOZZLE 235-245 MOLD TEMPERATURE 模溫 °C 50-70 INJECTION PRESSURE 射出*力 kg/cm2 600-1000 INJECTION SPEED 射出速度 - FAST