科思創(chuàng)Makrolon 6555

Density密度 1.20 g/cc 0.0434 lb/in? Water Absorption吸水率 0.35 % 0.35 % Saturation in water Moisture Absorption at Equilibrium吸濕平衡 0.15 % 0.15 % Equilibrium at 50% RH Water Absorption at Saturation飽和水吸收率 0.35 % 0.35 % Linear Mold Shrinkage 線(xiàn)性收縮率 0.0060 - 0.0080 cm/cm 0.0060 - 0.0080 in/in ASTM D955 Melt Flow熔體流動(dòng)速率 9.5 g/10 min @Load 1.20 kg, Temperature 300 °C 9.5 g/10 min @Load 2.65 lb, Temperature 572 °F Mechanical Properties力學(xué)性能 Metric公制數(shù)據(jù) English英制數(shù)據(jù) Comments測(cè)試方法 Hardness, Rockwell M羅氏硬度M 70 70 ASTM D785 Tensile Strength, Ultimate極限拉伸強(qiáng)度 69.0 MPa 10000 psi ASTM D638 Tensile Strength, Yield屈服拉伸強(qiáng)度 63.0 MPa 9140 psi Elongation at Break斷裂伸長(zhǎng)率 110 % 110 % ASTM D638 Elongation at Yield屈服伸長(zhǎng)率 6.0 % 6.0 % Tensile Modulus拉伸模量 2.40 GPa 348 ksi Flexural Yield Strength彎曲屈服強(qiáng)度 91.0 MPa 13200 psi at 5% strain; ASTM D790 Flexural Modulus彎曲彈性模量 2.30 GPa 334 ksi ASTM D790 Izod Impact, Notched懸臂梁缺口沖擊強(qiáng)度 8.50 J/cm @Thickness 3.20 mm 15.9 ft-lb/in @Thickness 0.126 in ASTM D256 Charpy Impact Unnotched夏比缺口試樣沖擊d NB NB Tensile Creep Modulus, 1 hour拉伸蠕變模量，1小時(shí) 2200 MPa 319000 psi Tensile Creep Modulus, 1000 hours 拉伸蠕變模量，1000小時(shí) 1900 MPa 276000 psi Electrical Properties電性能 Metric公制數(shù)據(jù) English英制數(shù)據(jù) Comments測(cè)試方法 Electrical Resistivity電阻率 >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm 聯(lián)系人：李先生 聯(lián)系方式：16621281687